Novel Polysiloxane and Polycarbosilane Aerogels via Hydrosilylation of Preceramic Polymers

Sorarù, Gian Domenico; Dalcanale, F.; Campostrini, Renzo; Gaston, A.; Blum, Y.; Carturan, S.; Aravind, P. R.

doi:10.1039/c2jm00020b

CINECA IRIS Institutional Research Information System

IRIS è l'Anagrafe della ricerca dell'Università degli Studi di Trento, e ha lo scopo di raccogliere, documentare, diffondere e conservare le informazioni relative alla produzione scientifica degli autori afferenti all'Università degli Studi di Trento.

We report new polysiloxane and polycarbosilane aerogels, which have been obtained by crosslinking Si–H-containing polymers with a C=C-containing crosslinker via hydrosilylation reactions. The crosslinking reaction has been carried out in a highly diluted solution using up to 97 vol% of solvent. The obtained aerogels have a colloidal structure with meso- and macropores. Density as low as 0.17 g cm3 has been reached, which implies a porosity of ca. 84 vol%.

Scheda prodotto non validato

I dati visualizzati non sono stati ancora sottoposti a validazione formale da parte dello Staff di IRIS, ma sono stati ugualmente trasmessi al Sito Docente Cineca (Loginmiur).

Titolo:	Novel Polysiloxane and Polycarbosilane Aerogels via Hydrosilylation of Preceramic Polymers
Autori Unitn:	Sorarù, Gian Domenico F. Dalcanale Campostrini, Renzo A. Gaston Y. Blum S. Carturan P. R. Aravind mostra contributor esterni nascondi contributor esterni
Anno di pubblicazione:	2012
Titolo del periodico:	JOURNAL OF MATERIALS CHEMISTRY
Citazione:	Novel Polysiloxane and Polycarbosilane Aerogels via Hydrosilylation of Preceramic Polymers / G. D. Sorarù; F. Dalcanale; R. Campostrini; A. Gaston; Y. Blum; S. Carturan; P. R. Aravind. - In: JOURNAL OF MATERIALS CHEMISTRY. - ISSN 0959-9428. - STAMPA. - 22(2012), pp. 7676-7680.
Abstract:	We report new polysiloxane and polycarbosilane aerogels, which have been obtained by crosslinking Si–H-containing polymers with a C=C-containing crosslinker via hydrosilylation reactions. The crosslinking reaction has been carried out in a highly diluted solution using up to 97 vol% of solvent. The obtained aerogels have a colloidal structure with meso- and macropores. Density as low as 0.17 g cm3 has been reached, which implies a porosity of ca. 84 vol%.
Handle:	http://hdl.handle.net/11572/91783
Appare nelle tipologie:	03.1 Articolo su rivista (Journal article)

File in questo prodotto:

Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione