The effectiveness of mechanically treated CeO 2 particles and SiO 2 particles as active fillers into an organic coating was investigated. For this purpose, different combinations of CeO 2 and SiO 2 particles were added to an epoxy-polyester polymeric matrix: mechanically treated CeO 2 particles, mechanically treated CeO 2/SiO 2 particles and mechanically treated SiO 2 powders (used for comparison). The particles were dispersed into the polymeric matrix and HDG steel panels were coated with the different paints. A strontium chromates containing paint was used as a reference to compare the performances of the other samples. The salt spray results proved the good performance of coatings containing combinations of ceria and silica especially where these had been mechanically treated in a co-milling operation. The paint containing only the mechanically treated SiO 2 particles showed a fairly good resistance in the salt spray chamber considering the scratched samples. The EIS measurements evidenced the good corrosion protection properties of the paints containing the different combinations of mechanically treated CeO 2 and SiO 2 particles. After about 1000 h of immersion in 0.1 M NaCl solution, the samples containing the mix of mechanically treated CeO 2/SiO 2 particles showed impedance values which were comparable with the chromate control sample. The cathodic polarization tests evidenced the low extent of detachment of the coating containing the mix of mechanically treated CeO 2/SiO 2 particles. The electrochemical characterization and neutral salt spray test results proved the effectiveness of the mechanical treated cerium (IV) oxides treated together with SiO 2 as active pigments to improve the corrosion protection of the substrate. The reasons for the synergistic effect of the milled (together or separately) SiO 2 and CeO 2 particles was not clear at all, but a few hypothesis were discussed. © 2011 Elsevier B.V. All Rights Reserved.
Study of the effect of mechanically treated CeO2 and SiO2 pigments on the corrosion protection of painted galvanized steel
Fedel, Michele;Deflorian, Flavio;Rossi, Stefano;
2012-01-01
Abstract
The effectiveness of mechanically treated CeO 2 particles and SiO 2 particles as active fillers into an organic coating was investigated. For this purpose, different combinations of CeO 2 and SiO 2 particles were added to an epoxy-polyester polymeric matrix: mechanically treated CeO 2 particles, mechanically treated CeO 2/SiO 2 particles and mechanically treated SiO 2 powders (used for comparison). The particles were dispersed into the polymeric matrix and HDG steel panels were coated with the different paints. A strontium chromates containing paint was used as a reference to compare the performances of the other samples. The salt spray results proved the good performance of coatings containing combinations of ceria and silica especially where these had been mechanically treated in a co-milling operation. The paint containing only the mechanically treated SiO 2 particles showed a fairly good resistance in the salt spray chamber considering the scratched samples. The EIS measurements evidenced the good corrosion protection properties of the paints containing the different combinations of mechanically treated CeO 2 and SiO 2 particles. After about 1000 h of immersion in 0.1 M NaCl solution, the samples containing the mix of mechanically treated CeO 2/SiO 2 particles showed impedance values which were comparable with the chromate control sample. The cathodic polarization tests evidenced the low extent of detachment of the coating containing the mix of mechanically treated CeO 2/SiO 2 particles. The electrochemical characterization and neutral salt spray test results proved the effectiveness of the mechanical treated cerium (IV) oxides treated together with SiO 2 as active pigments to improve the corrosion protection of the substrate. The reasons for the synergistic effect of the milled (together or separately) SiO 2 and CeO 2 particles was not clear at all, but a few hypothesis were discussed. © 2011 Elsevier B.V. All Rights Reserved.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione