On the shrinkage during pyrolysis of thin films and bulk components: the case of a hybrid silica gel precursor for SiOC glasses

Sorarù, Gian Domenico; Karakuscu, Aylin; Boissiere, C.; Babonneau, F.

doi:10.1016/j.jeurceramsoc.2011.10.004

CINECA IRIS Institutional Research Information System

IRIS è l'Anagrafe della ricerca dell'Università degli Studi di Trento, e ha lo scopo di raccogliere, documentare, diffondere e conservare le informazioni relative alla produzione scientifica degli autori afferenti all'Università degli Studi di Trento.

This paper compares the shrinkage during pyrolysis of a gel precursor as thin film and as bulk sample. The hybrid silica gel, precursor for SiOC glasses, contains Si–CH3 and Si–H moieties. The shrinkage of bulk samples has been measured with conventional dilatometry. Shrinkage of thin films has been studied for the first time with in situ dilatometry allowing to measure the thickness and the refractive index during pyrolysis. Thin films shrink more compared to bulk samples and the pyrolytic transformation occurs at lower temperature (100–150 ◦C) compared to the bulk samples.

Scheda prodotto non validato

I dati visualizzati non sono stati ancora sottoposti a validazione formale da parte dello Staff di IRIS, ma sono stati ugualmente trasmessi al Sito Docente Cineca (Loginmiur).

Titolo:	On the shrinkage during pyrolysis of thin films and bulk components: the case of a hybrid silica gel precursor for SiOC glasses
Autori Unitn:	Sorarù, Gian Domenico Karakuscu, Aylin Boissiere, C. Babonneau, F. mostra contributor esterni nascondi contributor esterni
Anno di pubblicazione:	2012
Titolo del periodico:	JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
Abstract:	This paper compares the shrinkage during pyrolysis of a gel precursor as thin film and as bulk sample. The hybrid silica gel, precursor for SiOC glasses, contains Si–CH3 and Si–H moieties. The shrinkage of bulk samples has been measured with conventional dilatometry. Shrinkage of thin films has been studied for the first time with in situ dilatometry allowing to measure the thickness and the refractive index during pyrolysis. Thin films shrink more compared to bulk samples and the pyrolytic transformation occurs at lower temperature (100–150 ◦C) compared to the bulk samples.
Handle:	http://hdl.handle.net/11572/90487
Appare nelle tipologie:	03.1 Articolo su rivista (Journal article)

File in questo prodotto:

Non ci sono file associati a questo prodotto.

Utilizza questo identificativo per citare o creare un link a questo documento:
http://hdl.handle.net/11572/90487

Citazioni

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione