Tensile Creep Behaviour of Polymethylpentene-Silica Nanocomposites

For the first time, poly(4-methyl-1-pentene) (PMP) nanocomposites were prepared by melt compounding 2 vol% of fumed silica nanoparticles, in order to study the role of the nanofiller surface area and functionalization on the tensile mechanical response of the material, with particular focus on its creep behaviour. The high optical transparency of the polymer matrix was substantially preserved in the nanocomposites, while the mechanical properties (in particular the creep stability) were improved. Dynamic mechanical thermal analysis showed an improvement of the storage modulus, more evident above the glass transition temperature of the polymer matrix. Uniaxial tensile tests evidenced that the elastic modulus of the material was positively affected by the presence of silica nanoparticles, even if a slight reduction of the strain at break was detected. The reduction of the tensile creep compliance was proportional to the surface area of the nanofiller, being more evident at high stresses and elevated temperatures. Findley’s law furnished a satisfactory fitting of the creep behaviour of the composites, even at high temperatures. It clearly emerges that the incorporation of fumed silica nanoparticles in PMP can be an effective way to overcome the problem of the poor creep stability of polyolefins, especially at high temperatures and high stresses. Moreover the possibility of retaining the original transparency of the material is fundamental for the production of completely transparent PMP components.