Conversion electron Mössbauer spectroscopy (CEMS) has been used to study tin oxide films prepared by sol-gel dipping and sputtering. The spectra of films prepared by sol-gel route result close to that of crystalline SnO2 after heat treatment at a temperature as low as 150°C. The Mössbauer parameters of as sputter deposited films indicate that the structure of the deposited stannic oxide has an amorphous character more pronounced for thinner samples. The structure becomes predominantly that of crystalline SnO2 by heating at 550°C for 30 min provided the film thickness is higher than 10 nm. © 1991 J.C. Baltzer A.G., Scientific Publishing Company.
CEMS characterization of SnO2 films obtained by sputtering and sol-gel route
Dal Maschio, Roberto;Dirè, Sandra
1991-01-01
Abstract
Conversion electron Mössbauer spectroscopy (CEMS) has been used to study tin oxide films prepared by sol-gel dipping and sputtering. The spectra of films prepared by sol-gel route result close to that of crystalline SnO2 after heat treatment at a temperature as low as 150°C. The Mössbauer parameters of as sputter deposited films indicate that the structure of the deposited stannic oxide has an amorphous character more pronounced for thinner samples. The structure becomes predominantly that of crystalline SnO2 by heating at 550°C for 30 min provided the film thickness is higher than 10 nm. © 1991 J.C. Baltzer A.G., Scientific Publishing Company.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione