Ni–Mo/Al composite coatings were obtained by electrodeposition from a Ni–Mo plating bath containing suspended Al particles. The factors including temperature, current density, and stirring rate aecting coating composition, wear, roughness, and morphology have been studied. It was found that properties such as hardness, roughness, wear, and the Al particle content showed parabolic behavior when changing each parameter. That means that there is a critical value for the mentioned parameters at which the properties of coatings become maximal.
Morphology, Hardness, and Wear Properties of Ni-Base Composite Coating Containing Al Particle / Mousavi, Rouhollah; Deflorian, Flavio; Bahrololoom, Mohammad Ebrahim. - In: COATINGS. - ISSN 2079-6412. - ELETTRONICO. - 10:4(2020). [10.3390/coatings10040346]
Morphology, Hardness, and Wear Properties of Ni-Base Composite Coating Containing Al Particle
Mousavi, Rouhollah;Deflorian, Flavio;
2020-01-01
Abstract
Ni–Mo/Al composite coatings were obtained by electrodeposition from a Ni–Mo plating bath containing suspended Al particles. The factors including temperature, current density, and stirring rate aecting coating composition, wear, roughness, and morphology have been studied. It was found that properties such as hardness, roughness, wear, and the Al particle content showed parabolic behavior when changing each parameter. That means that there is a critical value for the mentioned parameters at which the properties of coatings become maximal.| File | Dimensione | Formato | |
|---|---|---|---|
|
J183-C-20.pdf
accesso aperto
Tipologia:
Versione editoriale (Publisher’s layout)
Licenza:
Creative commons
Dimensione
5.6 MB
Formato
Adobe PDF
|
5.6 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione