Fatigue crack growth resistance and elastic–plastic fracture toughness were measured on MAG (Metal Active Gas) butt-welded joints made of S355JR construction steel. For this pur- pose, C(T) specimens were extracted from virgin and welded 15 mm thick rolled plates. Tests were conducted on the base material (BM), the heat affected zone (HAZ) and weld metal (WM). The analyses showed that compressive residual stresses due to welding increased the fatigue crack growth resistance of WM and HAZ owing to crack closure effects. The WM displayed the lowest elastic–plastic fracture toughness with respect to HAZ and BM. The highest value was exhibited by the HAZ because stable tearing crack extension is forced along an unfavourable crack path. Therefore, particular care must be taken in evaluating the crack path in welded joints in order to correctly estimate their resistance to crack advance. © 2013 Elsevier Ltd. All rights reserved.

Crack growth resistance of MAG butt-welded joints of S355JR construction steel / Benedetti, Matteo; Fontanari, Vigilio; C., Santus. - In: ENGINEERING FRACTURE MECHANICS. - ISSN 0013-7944. - STAMPA. - 108:(2013), pp. 305-315. [10.1016/j.engfracmech.2013.01.019]

Crack growth resistance of MAG butt-welded joints of S355JR construction steel

Benedetti, Matteo;Fontanari, Vigilio;
2013-01-01

Abstract

Fatigue crack growth resistance and elastic–plastic fracture toughness were measured on MAG (Metal Active Gas) butt-welded joints made of S355JR construction steel. For this pur- pose, C(T) specimens were extracted from virgin and welded 15 mm thick rolled plates. Tests were conducted on the base material (BM), the heat affected zone (HAZ) and weld metal (WM). The analyses showed that compressive residual stresses due to welding increased the fatigue crack growth resistance of WM and HAZ owing to crack closure effects. The WM displayed the lowest elastic–plastic fracture toughness with respect to HAZ and BM. The highest value was exhibited by the HAZ because stable tearing crack extension is forced along an unfavourable crack path. Therefore, particular care must be taken in evaluating the crack path in welded joints in order to correctly estimate their resistance to crack advance. © 2013 Elsevier Ltd. All rights reserved.
2013
Benedetti, Matteo; Fontanari, Vigilio; C., Santus
Crack growth resistance of MAG butt-welded joints of S355JR construction steel / Benedetti, Matteo; Fontanari, Vigilio; C., Santus. - In: ENGINEERING FRACTURE MECHANICS. - ISSN 0013-7944. - STAMPA. - 108:(2013), pp. 305-315. [10.1016/j.engfracmech.2013.01.019]
File in questo prodotto:
File Dimensione Formato  
EFM2013.pdf

Solo gestori archivio

Descrizione: Articolo principale
Tipologia: Versione editoriale (Publisher’s layout)
Licenza: Tutti i diritti riservati (All rights reserved)
Dimensione 2.85 MB
Formato Adobe PDF
2.85 MB Adobe PDF   Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11572/33028
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 18
  • ???jsp.display-item.citation.isi??? 18
social impact